{"_buckets": {"deposit": "1c5571d3-4b72-4463-b555-0195633aef52"}, "_deposit": {"id": "2689", "owners": [], "pid": {"revision_id": 0, "type": "recid", "value": "2689"}, "status": "published"}, "_oai": {"id": "oai:meral.edu.mm:recid/2689", "sets": ["user-uy"]}, "communities": ["ccm", "ccp", "kyauksetu", "ltc", "maas", "miit", "mlmu", "mmu", "mtlu", "mtu", "mub", "mude", "mufl", "pathein", "scu", "suoe", "tcu", "tgu", "tuh", "tum", "ucsm", "ucsmtla", "ucsmub", "ucspathein", "ucstaungoo", "ucsy", "udmm", "udmy", "uit", "um", "um1", "um2", "umkn", "umm", "uphy", "urj", "uvs", "uy", "yau", "ydbu", "ytu", "yude", "yueco", "yufl", "yuoe"], "control_number": "2689", "item_1583103067471": {"attribute_name": "Title", "attribute_value_mlt": [{"subitem_1551255647225": "Synthesis and Characterization of LaMnO3Nanofibers by Electrospinning Techique", "subitem_1551255648112": "en"}]}, "item_1583103085720": {"attribute_name": "Description", "attribute_value_mlt": [{"interim": "This paper aimed to prepare the synthesis of LaMnO3 nanofibers by electrospinning technique using a\r solution that contained polyvinyl alcohol (PVA) and a sol-gel solution of LaMnO3. LaMnO3/PVA perovskite-type\r nanofibers were obtained after annealed at 500°C, 600°C, 700°C and 800°C for 2h respectively. Thermal properties\r of LaMnO3 samples were examined by TG-DTA. Phase formation and crystal structure of LaMnO3 nanopowders\r were characterized by X-ray diffraction (XRD). FESEM images revealed that LaMnO3 as-spun nanofibers on Al\r foils were attracted to be between 60-120 nm in diameters with electrospinning set-up for 15 min. The crystal\r structure, fiber diameters and morphology of LaMnO3 nanofibers were influenced by the calcination temperatures.\r The qualifications of LaMnO3 nanofibers were successfully yielded by the electronspinning technique as final\r products."}]}, "item_1583103108160": {"attribute_name": "Keywords", "attribute_value_mlt": [{"interim": "Electrospinning set-up"}]}, "item_1583103120197": {"attribute_name": "Files", "attribute_type": "file", "attribute_value_mlt": [{"accessrole": "open_access", "date": [{"dateType": "Available", "dateValue": "2020-05-05"}], "displaytype": "preview", "download_preview_message": "", "file_order": 0, "filename": "Synthesis and Characterization of LaMnO3Nanofibers by Dr. Zin Min Myat.pdf", "filesize": [{"value": "403 Kb"}], "format": "application/pdf", "future_date_message": "", "is_thumbnail": false, "licensetype": "license_free", "mimetype": "application/pdf", "size": 403000.0, "url": {"url": "https://meral.edu.mm/record/2689/files/Synthesis and Characterization of LaMnO3Nanofibers by Dr. Zin Min Myat.pdf"}, "version_id": "504c1a44-4b5d-4ae4-976f-6769f641b508"}]}, "item_1583103131163": {"attribute_name": "Journal articles", "attribute_value_mlt": [{}]}, "item_1583103147082": {"attribute_name": "Conference papaers", "attribute_value_mlt": [{}]}, "item_1583103211336": {"attribute_name": "Books/reports/chapters", "attribute_value_mlt": [{}]}, "item_1583103233624": {"attribute_name": "Thesis/dissertations", "attribute_value_mlt": [{"subitem_supervisor(s)": []}]}, "item_1583105942107": {"attribute_name": "Authors", "attribute_value_mlt": [{"subitem_authors": [{"subitem_authors_fullname": "Zin Min Myat"}, {"subitem_authors_fullname": "Than Than Win"}, {"subitem_authors_fullname": "Yin Maung Maung"}, {"subitem_authors_fullname": "Ko Ko Kyaw Soe"}]}]}, "item_1583108359239": {"attribute_name": "Upload type", "attribute_value_mlt": [{"interim": "Publication"}]}, "item_1583108428133": {"attribute_name": "Publication type", "attribute_value_mlt": [{"interim": "Journal article"}]}, "item_1583159729339": {"attribute_name": "Publication date", "attribute_value": "2013"}, "item_1583159847033": {"attribute_name": "Identifier", "attribute_value": "http://uyr.uy.edu.mm/handle/123456789/35"}, "item_title": "Synthesis and Characterization of LaMnO3Nanofibers by Electrospinning Techique", "item_type_id": "21", "owner": "1", "path": ["1582967549708"], "permalink_uri": "http://hdl.handle.net/20.500.12678/0000002689", "pubdate": {"attribute_name": "Deposited date", "attribute_value": "2020-03-05"}, "publish_date": "2020-03-05", "publish_status": "0", "recid": "2689", "relation": {}, "relation_version_is_last": true, "title": ["Synthesis and Characterization of LaMnO3Nanofibers by Electrospinning Techique"], "weko_shared_id": -1}

Synthesis and Characterization of LaMnO3Nanofibers by Electrospinning Techique

http://hdl.handle.net/20.500.12678/0000002689
1715b085-6beb-44a3-9508-7fc202939bfd
1c5571d3-4b72-4463-b555-0195633aef52
None
Name / File License Actions
Synthesis Synthesis and Characterization of LaMnO3Nanofibers by Dr. Zin Min Myat.pdf (403 Kb)
Publication type
Journal article
Upload type
Publication
Title
Title Synthesis and Characterization of LaMnO3Nanofibers by Electrospinning Techique
Language en
Publication date 2013
Authors
Zin Min Myat
Than Than Win
Yin Maung Maung
Ko Ko Kyaw Soe
Description
This paper aimed to prepare the synthesis of LaMnO3 nanofibers by electrospinning technique using a
solution that contained polyvinyl alcohol (PVA) and a sol-gel solution of LaMnO3. LaMnO3/PVA perovskite-type
nanofibers were obtained after annealed at 500°C, 600°C, 700°C and 800°C for 2h respectively. Thermal properties
of LaMnO3 samples were examined by TG-DTA. Phase formation and crystal structure of LaMnO3 nanopowders
were characterized by X-ray diffraction (XRD). FESEM images revealed that LaMnO3 as-spun nanofibers on Al
foils were attracted to be between 60-120 nm in diameters with electrospinning set-up for 15 min. The crystal
structure, fiber diameters and morphology of LaMnO3 nanofibers were influenced by the calcination temperatures.
The qualifications of LaMnO3 nanofibers were successfully yielded by the electronspinning technique as final
products.
Keywords
Electrospinning set-up
Identifier http://uyr.uy.edu.mm/handle/123456789/35
Journal articles
Conference papaers
Books/reports/chapters
Thesis/dissertations
0
0
views
downloads
Views Downloads

Export

OAI-PMH
  • OAI-PMH DublinCore
Other Formats