Growth of TiO2-ZrO2 Binary Oxide Electrode for Dye Sensitized Solar Cell Application Than Than Win Aye Myint Myat Kywe Shwe Yee Win Honey Thaw Yin Maung Maung Ko Ko Kyaw Soe TiO2-ZrO2 fine binary oxide was prepared by mechanochemical milling process to be homogeneous binary oxide powder. TiO2-ZrO2 paste was deposited on microscopic glass slide by rolling. It was immersed in the henna solution and annealed at 100°C for 2h. It was deposited onto another glass slide and used as counter electrode (second electrode). Two glass slides were offset and two binder clips were used to hold the electrodes together. Photovoltaic properties of TiO2-ZrO2 cell were measured and it was expected to utilize the dye sensitized solar cells application. 2016 http://hdl.handle.net/20.500.12678/0000001785 https://meral.edu.mm/records/1785